Designation: D3732 − 82 (Reapproved 2017)Standard Practice forReporting Cure Times of Ultraviolet-Cured Coatings 1This standard is issued under the f i xed designation D3732; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (´) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This practice applies to all coatings cured by ultravioletenergy.1.2 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards: 2D658 Test Method for Abrasion Resistance of OrganicCoatings by Air Blast Abrasive (Withdrawn 1996) 3D968 Test Methods for Abrasion Resistance of OrganicCoatings by Falling AbrasiveD1474 Test Methods for Indentation Hardness of OrganicCoatingsD2197 Test Method for Adhesion of Organic Coatings byScrape AdhesionD2336 Guide for Specifying Factory Applied Wood Coat-ings (Withdrawn 2008) 3D2793 Test Method for Block Resistance of Organic Coat-ings on Wood Panel SubstratesD2794 Test Method for Resistance of Organic Coatings tothe Effects of Rapid Deformation (Impact)D3023 Practice for Determination of Resistance of Factory-Applied Coatings on Wood Products to Stains and Re-agentsD3281 Test Method for Formability of Attached OrganicCoatings with Impact-Wedge BendApparatus (Withdrawn1995) 3D3359 Test Methods for Rating Adhesion by Tape TestD3363 Test Method for Film Hardness by Pencil Test3. Terminology3.1 Def i nitions of Terms Specif i c to This Standard:3.1.1 cure, n—the condition of a coating after conversion tothe f i nal state of cure as measured by tests generally related toend-use performance and mutually agreeable to supplier andpurchaser.3.1.2 ultraviolet curing, n—conversion of a coating from itsapplication state to its f i nal use state by means of a mechanisminitiated by ultraviolet radiation generated by equipment de-signed for that purpose.4. Signif i cance and Use4.1 This practice provides a guide whereby all pertinentvariables relating to the ultraviolet cure of a coating aredescribed.5. Procedure5.1 Apply the coating to be cured to the desired substrate ata f i lm thickness typical to that normally used. After approxi-mately the time delay encountered in production pass thecoated substrate through the curing equipment and subse-quently test for cure, as def i ned in 3.1.1, using the appropriatemethods listed in 5.1.1 through 5.1.11. The most commonlyused test methods are listed in 5.1.1 through 5.1.4.5.1.1 Impact Resistance—Test Method D2794.5.1.2 Film Hardness—Test Method D3363.5.1.3 Solvent Rub Test—Hold a pad of cheesecloth or othercloth saturated with an agreed-upon solvent, usually methylethyl ketone, over two adjacent f i ngers using a protective1 This practice is under the jurisdiction of ASTM Committee D01 on Paint andRelated Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.55 on Factory Applied Coatings on Preformed Products.Current edition approved June 1, 2017. Published June 2017. Originallyapproved in 1978. Last previous edition approved in 2011 as D3732 – 82 (2011).DOI: 10.1520/D3732-82R17.2 For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at service@astm.org. For Annual Book of ASTMStandards volume information, refer to the standard’s Document Summary page onthe ASTM website.3 The last approved version of this historical standard is referenced onwww.astm.org.Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1 Copyright by ASTM Int'l (all rights reserved); Fri Oct 6 10:36:40 EDT 2017Downloaded/printed byUniversity of Edinburgh (University of Edinburgh) pursuant to License Agreement. No further reproductions authorized.
